Trans. Nonferrous Met. Soc. China
Vol.12  No.1            (Sum 46)          Feb.2002
［Article ID］1003-6326(2002)01-0127-05

Synthesis and thermal decomposition 
kinetics of LiNiO2

TIAN Yan-wen(田彦文),LI Hui(李  辉),ZHANG Xin(张  新),
ZHAI Yu-chun(瞿玉春),GAO Hong(高  虹)
(School of Materials and Metallurgy,Northeastern University,
Shenyang 110004,China)

［Abstract］A layered LiNiO2 with high crystallinity was synthesized by sintering the finely prepared mixture of lithium hydroxide and nickel hydroxide in the oxygen atmosphere. The electro-chemical properties of LiNiO2 show that it has a reversible capacity of more than 168mA·h·g-1.It was found that with increasing temperature,LiNiO2 decomposed in air followed with three reaction stages, the apparent activation energies were 747.18±1.0kJ·mol-1,932.46±1.0kJ·mol-1 and 1126.97 ±1.0kJ·mol-1 respectively,and the kinetic equations of the three reaction stages were obtained.

［Key words］lithiumion batteries;LiNiO2;electrochemistry;decomposition;kinetics
［CLC number］TM910.1
［Document code］A

［Foundation item］Project (9810300702) supported by Liaoning Science Fund Committee
［Received date］2001-04-09；［Accepted date］2001-06-25

　

From http://www.csu.edu.cn/ysxb/y2002a/yw2002-1/yw2002-1-028.html

　

140.30 光学

碱土金属铝酸盐系列长余辉磷光体的制备研究=Synthesis of MAl2O4∶Eu2+(M= Ca, Sr, Ba) Phosphors with Long Persistent Luminescence ［刊： 中］/翟玉春（东北大学冶金与材料物理化学研究所， 辽宁 沈阳 110004）, 张  新， 李建中， 田彦文∥中国稀土学报， 2003， 21(2)：205-208

    研究了MAl2O4∶Eu2+(M= Ca, Sr, Ba)磷光体的制备过程， 通过向磷光体中引入微量Dy3+, B3+等添加剂离子， 得到了发绿色光的超长余辉磷光体， 余辉发光初始亮度达4.8 cd·m-2， 激发停止50 h后， 其余辉发光仍清晰可见。 制备出发紫色光、 蓝色光及黄色光的碱土金属铝酸盐系列长余辉磷光体。 分析了各磷光体发射光谱、 激发光谱及余辉发光， 讨论了磷光体的光谱移动以及Eu2+在碱土金属铝酸盐中的发光。 图6  表2  参9

关键词： 功能材料； 长余辉磷光体； 高温合成； 多种发光颜色； 碱土金属铝酸盐； 填加剂； 稀土

辽宁省自然科学基金资助项目 （9910300501）

From http://cre-ol.com/jrechina/03chi01/ch0302.htm